Enhancement of Thermoelectric Performance through Transport Properties Decorrelation in the Quaternary Pseudo-Hollandite Chalcogenide Rb0.2Ba0.4Cr5Se8

International audience ; The novel quaternary compound Rb0.2Ba0.4Cr5Se8 was synthesized and characterized in both single crystal and polycrystalline forms. Crystallizing in the monoclinic crystal system (space group C2/m, cell parameters a = 18.7071(4) Å, b = 3.6030(1) Å, c = 8.9637(3) Å, β = 104.494(2)°) and isostructural to pseudo-hollandite compounds, it features mixed Rb and Ba occupancy within its one-dimensional channels. High-temperature X-ray diffraction revealed no decomposition up to 973 K, and the thermal expansion coefficient at 300 K was determined to be 2.6(1)·10$^