The sintering features are investigated in the article for the ceramic materials which were obtained by semidry compacting of the potassium polytitanate precursor powder modified by cobalt compounds and preprocessed by the heat treatment at 700 °C. The phase composition, thermomechanical and electrochemical properties were studied for the samples synthesized at 700, 940 and 1100 °C. The sintering mechanism and its influence on the ceramics properties were analyzed for the investigated ceramic samples at various temperatures. It was stated that the ceramic samples sintered at the temperature nomore than 750 °C have the best properties at 700 °C. The possibility is regarded to use the obtained type ceramics as the part of thermoelectric and thermoelectrochemical unitsdesigned for the thermal vessels' dissipated heat energy storage at the metallurgical enterprises. Ill. 4. Ref. 8. Tab. 1. ; Изучены особенности процесса спекания керамических материалов, полученных методом полусухого прессования при использовании в качестве порошка-прекурсора полититаната калия, модифицированного соединениями кобальта и прошедшего предварительную термическую обработку при 700 °С. Исследован фазовый состав, термомеханические и электрофизические свойства образцов керамики, синтезированных при 700, 950 и 1100 °С. Проанализированы механизм процессов, протекающих при спекании исследованной керамики при различных температурах, и его влияние на свойства полученной керамики. Показано, что при 700 °С оптимальными свойствами обладают образцы керамики, спеченной при температуре не выше 750 °С. Рассматривается возможность использования керамики полученного типа в составе термоэлектрических и термоэлектрохимических устройств, предназначенных для аккумуляции энергии рассеянного тепла печного оборудования металлургических производств.